ARCFCW9996
Material class: high anti-wear welding wire
Material symbols: high carbon, high chromium, FeNb-based hard alloy,
Carbon content: 5.8%
Chromium content: 22.0%
Other metal: Mo, Nb, Mn, Si, etc.
Hardness of the welding wire: about 59-65 HRC
Characteristic:
1. After welding, the reacted compound carbide distributes in the base part of workpiece
2. As it can produce tiny,hard niobium carbide, which makes the primary carbide overlayed material has highly anti-wear performance.
3. General anti-impusive force performance
4. Strong anti-falls, not suitable for cutting by fire,
5. Can not be mechanical processed.
6. The application temperature should not beyond 650℃
Recommendation:
Suitable for the hardfacing treatment of workpiece that need to endure strong wear and medium impulsive force,like weld repair,thermal mill roller/segment repair,cement vertical mill roller/segment, pulverizer roller repair,crusher hammer repair. It is also suitable for manufacturing the compound steel plate and overlaying the compound roller.
Specification: Φ2.0mm, Φ2.4mm, Φ2.8mm, Φ3.2mm
Package: cargo in roll: 25kg/roll, 50kg/roll, 200kg/barrel
|