Material class: high anti-wear hard-facing material

Material Symbol: High chrome carbide, Nb based hard alloy

Carbon Content: 5.6%

Chromium Content: 24%

Hardness of the welding wire: 58-64 HRC

Characteristics:

1, After welding, the reacted compound carbide distributes in the base part of workpiece
2, As it can produce tiny, hard niobium carbide, which makes the primary carbide overlayed material has highly anti-wear performance.
3, General wear-resistant
4, Not suitable for flame cutting, strong anti-falls
5, Can not be mechanical processed, otherwise it will appear cracks
6, The application temperature should below 650°C

Recommendation:

Suitable for hard-facing treatment of workpiece which need to endure strong wear and medium impulsive force: weld repair, thermal mill roller/segment repair, cement vertical mill roller/segment, pulverizer roller repair, crusher hammer repair, also suitable for manufacturing the composite steel plate and overlaying the composite roller.

Reference standard: BS EN14700:2005

Specification: Φ2.0mm, Φ2.4mm, Φ2.8mm, Φ3.2mm

Package: cargo in roll: 25KG/roll, 50KG/roll, 200KG/barrel
Welding note: inert gas is not necessary, AC/DC, the arc should be as short as possible